Fire Clay Brick for Coke Oven

Fire Clay Brick for Coke Oven
Features:
1) Fire clay checker brick JN40a for coke oven:
a) Al 2O3 (%): 40
b) Fe 2O3 (%): 2.0
c) Refractoriness (SK): 32
d) Refractoriness under load, 0.2MPa, Ta, (o C):1450
e) Porosity (%): 22
f) Bulk density (g/cm&up 3;): 2.0
g) Cold crushing strength (Mpa): 35
h) Thermal expansion at 1000o C (%):0.6
2) Fire clay checker brick JN406 for coke oven:
a) Al 2O3 (%): 40
b) Fe 2O3 (%): 2.0
c) Refractoriness (SK):32
d) Refractoriness under load, 0.2MPa, Ta (o C): 1,400
e) Porosity, (%): 24
f) Bulk density (g/cm&up 3;): 2.0
g) Cold crushing strength (Mpa): 30
h) Thermal expansion at 1,000o C (%): 0.6
3) Special alumina brick JLZ-75:
a) Al 2O3 (%): 75
b) Fe 2O3 (%): 2.0
c) Refractoriness, SK: 36
d) Refractoriness under load, 0.2MPa, KD (o C): 1,550
e) Permanent change at 1,500o Cx 2hrs. (%):+0.1 - -0.4
f) Porosity (%): 20
g) Bulk density (g/cm&up 3;): 2.65
h) Cold crushing strength (Mpa): 65
i) Creep at 0.2MPax 50hrs x 1,500o C, (%): 0.5
4) Special alumina brick JHL-75:
a) Al 2O3 (%): 75
b) Fe 2O3 (%): 0.8
c) Refractoriness, SK: 36
d) Refractoriness under load, 0.2MPa, KD, o C: 1,650
e) Permanent change at 1,500o Cx 2hrs, (%):0 - +0.1
f) Porosity, (%): 18
g) Bulk density (g/cm&up 3;): 2.65
h) Cold crushing strength (Mpa): 90
i) Creep at 0.2MPa x (20-50) hrs. x 1,500o C, (%):0.2
5) Alumina - sillimanite brick LS-60:
a) Al 2O3 (%): 60
b) Refractoriness (SK): 36
c) Refractoriness under load, 0.2MPa, T2, (o C): 1,500
d) Permanent change at 1400 0Cx 2hrs, (%): &lusmn;0.2
e) Porosity (%): 22
f) Cold crushing strength (Mpa): 50
g) Thermal sh (o C) k resistance at 1,100o C in
water, cycles: 20
6) Alumina - sillimanite brick LS-65:
a) Al 2O3 (%): 65
b) Refractoriness (SK): 36
c) Refractoriness under load, 0.2MPa, T2, (o C): 1,550
d) Permanent change at 1,400o Cx 2hrs, (%): &lusmn;0.2
e) Porosity (%): 22
f) Cold crushing strength (Mpa): 50
g) Thermal sh (o C) k resistance at 1,100o C in
water (cycles): 20
7) Andalusite brick HS-55:
a) Al 2O3 (%): 55
b) Refractoriness (SK): 35
c) Refractoriness under load, 0.2MPa, T2, o C: 1,450
d) Permanent change at 1,400o Cx 2hrs, (%): &lusmn;0.2
e) Porosity (%): 22
f) Cold crushing strength (Mpa): 50
g) Thermal sh(o C) k resistance at 1,100o C in
water, (cycles): 20
8) Cordierite brick SPCD-50:
a) Al 2O3 (%): 50
b) Refractoriness (SK): 35
c) Porosity (%): 24
d) Cold crushing strength (Mpa): 40
e) Thermal sh(o C) k resistance at 1,100o C in
water, (cycles): 12
f) Thermal expansion at 1,000o C, (%): 0.5
9) Sintered-mullite brick MZ-60:
a) Al 2O3 (%): 60
b) Fe 2O3 (%): 1.2
c) Refractoriness (SK): 36
d) Bulk density (g/cm&up 3;): 2.45
e) Refractoriness under load, 0.2MPa, T2, o C: 1,600
f) Permanent change at 1,500o Cx 3hrs, (%): &lusmn;0.1
g) Porosity (%): 20
h) Cold crushing strength (Mpa): 50
10) Sintered-mullite brick MZ-75:
a) Al 2O3 (%): 75
b) Fe 2O3 (%): 0.6
c) Refractoriness (SK): 36
d) Refractoriness under load, 0.2MPa, T2, o C: 1,700
e) Bulk density (g/cm&up 3;): 2.6
f) Permanent change at 1,500o Cx 3hrs., (%): &lusmn;0.1
g) Porosity (%): 20
h) Cold crushing strength (Mpa): 60
11) Crundunm - mullite brick GMS - 80:
a) Al 2O3 (%): 80
b) Fe 2O3 (%): 0.5
c) Refractoriness (SK): 36
d) Refractoriness under load, 0.2MPa, T2, (o C): 1,700
e) Permanent change at 1500 0C x 3hrs., (%): &lusmn; 0.1
f) Porosity (%): 20
g) Cold crushing strength (Mpa): 60

Please use contact form for send message directly to seller. Your message will be sent directly to the recipient and will not be publicly displayed.

Advertisement

Try related keywords

furniture
bamboo chair
bamboo product
ab lounge
chair
bamboo table
outdoor furniture
home furniture
bamboo cabinet
aa battery
abs case
ab scissor
ab chair
bamboo flooring
ab exerciser
More...
Post your product now!

Trade Alert

Tell me about new porducts and suppliers in:
RSS Feeds


See also...